Product name | Color | Physical state | packaging |
Volume (g/cm3) |
Operation time limit (25¡æ) |
Curing time (25¡æ) |
BD403 reactor still repair putty compound | Gray | Semi-fluid | 400g/set | 364 | 45 min | 24 hours |
Density (g/cm3) |
Compressive strength (kg/cm2) GB1041-2008 |
Tensile strength (kg/cm2) GB6329-1999 |
Shear strength (kg/cm2) GB7124-2009 |
Bending strength (kg/cm2) GB1042-2008 |
Hardness £¨Shore D£© ASTM-D-2556 |
Working temperature (dry state) (¡æ) |
1.38 | 1004 | 353 | 254 | 562 | 86 | -60-150 |
hydrochloric acid | phosphoric acid | sodium hypochlorite | lime water | sodium hydroxide |
30% | 30% | 15% | 50% | 50% |
Heat the briquette up to 80¡æ for curing,place into the above medium at room temperature for 30 days,the change of weight is not more than 1% |